Inconel 702
2021-03-30 08:20:35 Origin： Remark：0 Click：
Specifications Inconel 702 Round bar, Flat bar Inconel 702 Forgings, Sheet Properties Steelmelting (ESR / VAR refined), Hot forging, Hot rolling, Heat treatment.
MATERIAL TECHNICAL STANDARD - Grade Inconel 702
MATERIAL CATEGORY - High Alloy Aerospace Material Steel Series
TECHNICAL SPECIFICATION - AMS 6527E
HS CODE - 72221100 / 72221900 / 72223000
TECHNICAL SPECIFICATION - AMS 6527E
HS CODE - 72221100 / 72221900 / 72223000
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.10
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.10
Manganese, Mn (％): ≤ 1.00
Silicon, Si (％): ≤ 0.70
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Silicon, Si (％): ≤ 0.70
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (%): Remainder
Molybdenum, Mo (％): -
Molybdenum, Mo (％): -
Cobalt, Co (%): ≤ 1.00
Titanium, Ti (％): 0.25 ~ 1.00
Aluminum, Al (％): 2.75 ~ 3.75
Copper, Cu (%): ≤ 0.50
Copper, Cu (%): ≤ 0.50
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: bars and forgings
Tensile strength, σb/MPa: 910
Yield strength, σ0.2/MPa: 660
Form: bars and forgings
Tensile strength, σb/MPa: 910
Yield strength, σ0.2/MPa: 660
Elongation, δ(％): 35.0
Reduction of area, ф(％): 60.0
Hardness + solution annealed (HB): -
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
DIMENSIONS AND FORMS
Round bar & Disc (diameter): 5.5mm ~ 850mm
Square bar / flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Reduction of area, ф(％): 60.0
Hardness + solution annealed (HB): -
MELTING PROCESS & APPLICATION
This alloy is generally smelt in BEF or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
DIMENSIONS AND FORMS
Round bar & Disc (diameter): 5.5mm ~ 850mm
Square bar / flat bar: 10mm to 500mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 500mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.