AMS 5764
2021-04-30 14:55:17   Origin:   Remark:0 Click:

Aerospace AMS 5764 Specifications, Datasheet AMS 5764 Chemical, AMS 5764 Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade AMS 5764

OFFICIAL TEST CERTIFICATE - issued by TUV - SGSBV
MATERIAL CATEGORY - Austenitic Stainless Steel bar
Technical standards - SAE AMS 5764D
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     ≤ 0.060
Si (%):     ≤ 1.00
Mn (%):   4.00 ~ 6.00
P (%)≤:   0.040
S (%)≤:   0.030
Cr (%):    20.5 ~ 23.5
Ni (%):    11.5 ~ 13.5
Mo (%):   1.50 ~ 3.00
Nb (%):   0.10~0.30
N (%):     0.20 ~ 0.40
V (%):     0.10 ~ 0.30 
MECHANICAL PROPERTIES UNDER ROOM TEMP. 
Tensile strength, σb/MPa: 690 min.
Yield strength, σ0.2/MPa: 380 min.
Elongation, δ (%): 35.0 min.
Reduction area, ф (%): 55 min.
Hardness (HBW):  -
Hardness | HRB:  -
Cold bending property: None
 
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 400mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.

Form: wire or straightened bar

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers.- Email:
sales@ccsteels.com.

Hot search:AMS 5764

Previous page:AMS 5561
Last page:AMS 5563

Share to: