X5CrNiMoCuNb14-5 / 1.4594
2025-05-07 10:26:45 Origin： Remark：0 Click：
EN 10088-3 Martensitic Precipitation hardening Steel X5CrNiMoCuNb14-5 Round bar, Flat bar, S143 ESR ingot stock, 1.4594 Hot forging / rolling, Ageing heat treated
MATERIAL DESIGNATION - X5CrNiMoCuNb14-5 & 1.4594
Material category - Hardening precipitation steels
Material specifications - DIN EN 10088-3, 10297,10272,10312,10088-5(2005)
Official Test Certificate - EN 10204 - 3.1 MTR
HS Code For Customs - 72224000 / 72223000 / 72221100
Inventory - diam. 60 ~ 130mm, ESR ingot.
Inventory - diam. 60 ~ 130mm, ESR ingot.
Typical chemical compositions (mass fraction %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 13.0 ~ 15.0
Molybdenum, Mo (％): 1.20 ~ 2.00
Nickel, Ni (％): 5.00 ~ 6.00
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 13.0 ~ 15.0
Molybdenum, Mo (％): 1.20 ~ 2.00
Nickel, Ni (％): 5.00 ~ 6.00
Niobium, Nb (%): 0.15 ~ 0.60
Copper, Cu (%): 1.20 ~ 2.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Hardness HBW under annealed : 366 max.
Yield strength, Rp0.2 ≥ MPa: 720
Tensile strength, Rm / MPa: 930
Elongation, A5 ≥ (％): 15.0
Impact absorbing power Akv ≥ J | lengthways : -
Impact absorbing power Akv ≥ J | crosswise: -
Tensile strength, Rm / MPa: 930
Elongation, A5 ≥ (％): 15.0
Impact absorbing power Akv ≥ J | lengthways : -
Impact absorbing power Akv ≥ J | crosswise: -
PRODUCT DESCRIPTION
X5CrNiMoCuNb14-5 is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment + aged.
X5CrNiMoCuNb14-5 is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment + aged.
Medical equipments and Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolts, nuts, and pressure vessel.
Bolts, nuts, and pressure vessel.
PROFILE & DIMENSIONS
Rod / round bar / disc (diameter): 5.5mm to 900mm
Square bar / flat bar: 8mm to 600mm
Rod / round bar / disc (diameter): 5.5mm to 900mm
Square bar / flat bar: 8mm to 600mm
Length: random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 5000mm
Heavy / middle plate via hot rolled: T60 - 450mm X W50 - 1000mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers.
Hot search：X5CrNiMoCuNb14-5 & 1.4594
Previous page：1.4594 / X5CrNiMoCuNb14-5 Steel EN 10088-3
Last page：最后一页