X12CrNiMoV12-2
2019-05-27 10:22:36 Origin： Remark：0 Click：
X12CrNiMoV12-2 Martensitic steel, X12CrNiMoV12-2 Chemical, X12CrNiMoV12-2 Properties from steelmaking, X12CrNiMoV12-2 forging, rolling, heat treatment, cold working. We possess advanced precision machining equipments for the best service and quotation.
TECHNICAL DATASHEET - Grade X12CrNiMoV12-2
MATERIAL CATEGORY: 12Cr-3Ni-Mo-V alloy steel
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10 ~ 0.14
Si (％): ≤ 0.40
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Ni (％): 2.00 ~ 3.00
Mo (％): 1.00 ~ 2.00
Si (％): ≤ 0.40
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Ni (％): 2.00 ~ 3.00
Mo (％): 1.00 ~ 2.00
Nb (%): 0.05 ~ 0.40
V (％): 0.25 ~ 0.40
V (％): 0.25 ~ 0.40
N (%): 0.020 ~ 0.040
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: annealing
Tensile strength, TS, σb/MPa: 930 ~ 1100
Yield strength, YS, σ0.2/MPa: 795
Yield strength, YS, σ0.2/MPa: 795
Elongation, EL, δ(％): 15.0
Reduction of area, AZ, ф(％): 50.0
Hardness | HRB: 285 ~ 331
Reduction of area, AZ, ф(％): 50.0
Hardness | HRB: 285 ~ 331
condition of heat treatment: HT:955℃~1022℃ air/oil cooling, >=565℃ X 2h tempering
Tensile strength, TS, σb/MPa: 1000
Yield strength, YS, σ0.2/MPa: 795
Yield strength, YS, σ0.2/MPa: 795
Elongation, EL, δ(％): 17.0
Reduction of area, AZ, ф(％): 35.0
Hardness | HRB: 302~352
Reduction of area, AZ, ф(％): 35.0
Hardness | HRB: 302~352
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + ESR / EAF + VD + LF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by BEF + ESR / EAF + VD + LF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the annealed condition.
Final heat treatment - solution treatment
FORMS AND SHAPES
Round bar / Flat bar: 10 ~ 520mm
Sheet steel via cold rolled: T1.0 - 4mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W10 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T1.0 - 4mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W10 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to E-MAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to E-MAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：X12CrNiMoV12-2
Previous page：X21CrMoV12-1
Last page：X6NiCrTiMoVB25-15-2
Total list
Monthly rank
- 48Carpenter 20 Mo 6
- 18Aquamet 22
- 16UNS N06025
- 16Hastelloy G-2 / N06975
- 13Incoloy 840
- 12BG-42
- 12Custom 475
- 1210705BU
- 121.4938
- 11Aquamet 17