ASTM A565 martensitic stainless steel S64152 hardened round bar, flat bar, plate, hexagon bar, hot forged & rolled, 1022℃ quenched, cold finished
TECHNICAL DATA SHEET - UNS S64152
Stock in hand: round bar 50 ~ 210 mm
Typical chemical elements (mass weight - %)
Carbon, C (％): 0.08 ~ 0.15
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
PHosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
PHosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.025
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 2.00 ~ 3.00
Molybdenum, Mo (％): 1.50 ~ 2.00
Vanadium, V (％): 0.25 ~ 0.40
Nitrogen, N (%): 0.01 ~ 0.05
Condition of heat treatment: annealing
Hardness, HB: ≤ 311
Condition of heat treatment: HT 955 ~ 1022℃ air / oil cooling, ≥ 565℃, 2h tempering
Tensile strength, σb / MPa: 1000
Yield strength, σ0.2 / MPa: 795
Yield strength, σ0.2 / MPa: 795
Elongation, 5δ : 13.0
Reduction of area, Z : 35.0
Hardness | HBW: 302 ~ 352
Reduction of area, Z : 35.0
Hardness | HBW: 302 ~ 352
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / AOD followed by electroslag refining (ESR or VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the annealed condition.
Final heat treatment - Quenched and tempered, + SRA.
The alloy is usually produced by EAF / AOD followed by electroslag refining (ESR or VAR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the annealed condition.
Final heat treatment - Quenched and tempered, + SRA.
SHAPES AND DIMENSIONS
Round bar, rod, disc: 6.0 ~ 900 mm
Heavy/middle plate via hot forged / rolled: T6 ~ 350 x W15 ~ 1000 x Lmm
Sheet steel via cold rolled: T1.0 - 4 X W20 ~ 300 x L1000 ~ 2000 mm
Steel strip via cold rolled: T0.5 ~ 3 x W10 ~ 200 x L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T1.0 - 4 X W20 ~ 300 x L1000 ~ 2000 mm
Steel strip via cold rolled: T0.5 ~ 3 x W10 ~ 200 x L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
Further, please also check the materials in stock available:
Raw material - steels of blade for steam turbine
XM-25, S45000, GD450, C450
403 ESR, GB8732 type 12Cr12Mo, 10705BA/BB/BC
AISI 616, 422, 1.4935, X20CrMoWV12-1, 10705BU
B50A365B, 403Cb+, 1.4913, X19CrMoVNbN11-1
17-4PH, 630, 1.4542, X5CrNiCuNb16-4, 10705GU/GV/GW
M-152, S64152, 1.4938, X12CrNiMoV12-3, S151D
FV520B, S143, 1.4594, X4CrNiCuMo14-5
X22CrMoV12-1, 1.4923
13Х11Н2B2MФ, AE961W
15-5PH, XM-12, S15500
A286, AISI 660, S66286
10705MBU, 10705AJ
Non-magnetic 18.0% Manganese alloy steel:
1.3813, X40MnCrN19
1.3816, X8MnCrN18-18
1.3817, X40MnCr18
1.3818, X55MnCrN18-4
Hot search：
Previous page：15.0Cr Ferritic steel 429
Last page：最后一页