1.4300 /DIN X12CrNi18-8
2014-11-20 16:39:31 Origin： Remark：0 Click：
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 17.0 ～ 19.0
Ni (％): 8.00 ～ 9.00
Mo (％): —
Other (％): N≤0.10
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 130
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 105
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaf
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: email@example.com
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.