X2CrNiMoCuWN25-7-4
2025-06-12 02:32:00 Origin： Remark：0 Click：
Technical specifications of DIN X2CrNiMoCuWN25-7-4 austenitic stainless steel - Chemical composition,
mechanical properties from steelmaking, hot forging, rolling, heat treatment
TECHNICAL DATA SHEET - X2CrNiMoCuWN25-7-4
MATERIAL CATEGORY: Austenitic-ferritic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297, 10312, DIN EN 10088-5(2005)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 24.0 ~ 26.0
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 24.0 ~ 26.0
Nickel, Ni (％): 6.00 ~ 8.00
Molybdenum, Mo (％): 3.00 ~ 4.00
Other (％): Nitrogen 0.20 ~ 0.30, Copper 0.50~1.00, Tungsten 0.50 ~ 1.00
Molybdenum, Mo (％): 3.00 ~ 4.00
Other (％): Nitrogen 0.20 ~ 0.30, Copper 0.50~1.00, Tungsten 0.50 ~ 1.00
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness/mm:-
Tensile strength, σb / MPa: 740
Yield strength, σ0.2 ≥ MPa: 550
Elongation, δ5 ≥ (％): 15
Reduction of area, ψ ≥ (％): -
Impact strength, Akv ≥ J: 90
Yield strength, σ0.2 ≥ MPa: 550
Elongation, δ5 ≥ (％): 15
Reduction of area, ψ ≥ (％): -
Impact strength, Akv ≥ J: 90
Hardness HBS30: -
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1150~850
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1070~1150 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: solution treatment
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.