Specifications X2CrMoTi17-1 datasheet, X2CrMoTi17-1 Chemical, X2CrMoTi17-1 properties from steelmaking, hot forging, hot rolling, heat treatment,cold working.We also possess advanced precision machining equipments for further processing
MATERIAL DATA SHEET - DIN X2CrMoTi17-1
MATERIAL CATEGORY - Common alloy steel - Ferritic corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440, EN 10088-1, 10297,10272,10312, EN 10088-5
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.025
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 16.0 ~ 18.0
Ni (％): —
Mo (％): 0.80 ~ 1.40
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 16.0 ~ 18.0
Ni (％): —
Mo (％): 0.80 ~ 1.40
Ti (%): 0.30 ~ 0.60
Others (％): N ≤0.20
Others (％): N ≤0.20
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: annealed
Thickness/mm:-
Tensile strength, σb/MPa: 390 ~ 560
Yield strength, σ0.2≥/MPa: 220
Elongation, δ5≥(％): 20
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: 70
Yield strength, σ0.2≥/MPa: 220
Elongation, δ5≥(％): 20
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: 70
Hardness HBS30: 180max.
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: 750~850 air/water cooled
Heat treatment temperature and cooling methods|quenching: -
Heat treatment temperature and cooling methods|tempering: -
Condition: annealed
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: 230
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 200
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: 200
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: 190
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 180
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: 180
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
AVAILABILITY
Round bar / flat bar / steel strip / square bar / ring
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Round bar / flat bar / steel strip / square bar / ring
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mmLength: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mmLength: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.