Specifications EN 10088-1 of grade X12CrNiWTiB16-13 sheet, round bar, plate 1.4962 steelmaking, ESR, blooming, forging, rolling, heat treatment, straightened, ultrasonic test.
TECHNICAL DATA SHEET of Creep-resisting steel - X12CrNiWTiB16-13
MATERIAL CATEGORY: austenitic creep-resisting steel
FEATURES AND CLASSIFICATIONS
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095 (2002/1999), EN 10088-1 (2005)
TYPICAL CHEMICAL COMPOSITIONS (mass weight- %)
Carbon, C (％): 0.07 ~ 0.15
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.015
Carbon, C (％): 0.07 ~ 0.15
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 15.5 ~ 17.5
Molybdenum, Mo (％): -
Nickel, Ni (％): 12.5 ~ 14.5
Titanium, Ti (%): 0.40 ~ 0.70
Vanadium, V (%): -
Tungsten, W (%): 2.50 ~ 3.00
Boron, B (％): 0.0015 ~ 0.0060
Boron, B (％): 0.0015 ~ 0.0060
MECHANICAL PROPERTIES AT ROOM TEMPERATURE
Condition: solution treatment
Tensile strength, σb / MPa: 500 ~ 710
Condition: solution treatment
Tensile strength, σb / MPa: 500 ~ 710
Yield strength, σs ≥ MPa: 330
Elongation, δ5 ≥ (％): 35.0
Elongation, δ5 ≥ (％): 35.0
Non-scale temperature in air ℃: 750
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers - E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers - E-mail: sales@ccsteels.com
PRODUCT PROFILE AND DIMENSIONS
Round bar & rod & disc (diameter): 6.0 to 850 mm
Square bar & flat bar: 10mm to 800mm
Length: random length or based on the customer's special requirement.
Round bar & rod & disc (diameter): 6.0 to 850 mm
Square bar & flat bar: 10mm to 800mm
Length: random length or based on the customer's special requirement.
Heavy/middle plate: T6 ~ 400mm X W20 ~ 1000 X L1000 ~ 5000 mm
Sheet steel via cold rolled: T0.5 ~ 6mm X W15 ~ 1000 X L1000 ~ 2000mm
Steel strip via cold rolled: T0.3 ~ 3 X W10 ~ 200 X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 ~ 6mm X W15 ~ 1000 X L1000 ~ 2000mm
Steel strip via cold rolled: T0.3 ~ 3 X W10 ~ 200 X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.