1.3914
2025-04-06 10:54:00 Origin： Remark：0 Click：
Specification 1.3914 Round bar datasheet, 1.3914 Ring forging Bar steelmaking, ESR, Hot blooming, 1.3914 hot Forging & Rolling, Heat treatment
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATION - WS 1.3914
MATERIAL CATEGORY: Non-magnetic stainless steel and alloy
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991)
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): 6.00 ~ 8.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 20.0 ~ 22.0
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): 6.00 ~ 8.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 20.0 ~ 22.0
Nickel, Ni (％): 14.0 ~ 16.0
Molybdenum, Mo (％): 3.00 ~ 3.50
Niobium, Nb (％): 0.10 ~ 0.25
Molybdenum, Mo (％): 3.00 ~ 3.50
Niobium, Nb (％): 0.10 ~ 0.25
Nitrogen, N (%): 0.35 ~ 0.50
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 950℃
Quenching or solution treatment temperature: 1020~1120℃
Tensile strength, σb ≥ MPa: 880 ~ 1050
Yeild strength, σ0.2 ≥ MPa: 510
Elongation, δ5 ≥ (％): 30.0
Yeild strength, σ0.2 ≥ MPa: 510
Elongation, δ5 ≥ (％): 30.0
Impact, Akv ≥ J: 55 (transversal value)
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied peeled bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VD / followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied peeled bright in the annealed condition.
Final heat treatment - solution treatment / QT
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE
Round bar / disc (diameter): 5.5mm to 800mm
Square bar / flat bar: 8mm to 600mm
Round bar / disc (diameter): 5.5mm to 800mm
Square bar / flat bar: 8mm to 600mm
Wire rod (Diameter): 5.5mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email our resident team of qualified production engineers. E-mail: sales@ccsteels.com