EN 1.4508
2015-04-23 10:58:58 Origin： Remark：0 Click：
Flat bar EN 1.4508 Ring, Forgings EN 1.4508 Round bar, X2CrNiMoCuN25-6-3 Wire rod, Sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS EN 10088-3 (2005) or By agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade BS X2CrNiMoCuN25-6-3 / 1.4508
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE: Austenite - ferrite / Duplex type
MATERIAL SPECIFICATIONS: BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (Mass weight - %)
C (％): ≤ 0.030
Si (％): ≤ 0.70
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 24.0 ~ 26.0
Ni (％): 6.00 ~ 8.00
Mo (％): 3.00 ~ 4.00
Si (％): ≤ 0.70
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.015
Cr (％): 24.0 ~ 26.0
Ni (％): 6.00 ~ 8.00
Mo (％): 3.00 ~ 4.00
N (％): 0.20 ~ 0.30, Cu 1.00 ~ 1.50
MECHANICAL PROPERTIES VIA SOLUTION TREATMENT
Thickness Diameter (d)/≤mm: 160
Hardness HBS: 270
Yield strength σ0.2≥/MPa: 500
Tensile strength σb/MPa: 700～900
Yield strength σ0.2≥/MPa: 500
Tensile strength σb/MPa: 700～900
Elongation δ(longitudinal )≥(％): 25
Impact absorbing energy Akv≥/J|longitudinal: 100
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
Intergranular corrosion resistance tendency | condition of welding: Yes
DUPLEX STAINLESS STEEL / CHARACTERS
Duplex (ferrite-austenite) stainless steels maintain properties both ferritic steel and austenitic steel and possess the feature of superplasticity, which have each half austenitic and ferritic structures. Under the circumstances of lower carbon content, chromium content 18% ~ 28%, Nickel content 3%~10%. Some other steels contain the alloy elements - Mo, Cu, Si, Nb, Ti, N and so on. Those steels possess the properties of austenite and ferrite steels. Compared with ferritic steels, duplex stainless steels have good plasticity and toughness, non-room temperature fragility, intergranular corrosion resistance and weldability, and also maintain the features of ferritic stainless steel 475℃ frangibility, a higher heat conductivity coefficient, superplasticity. Compared with austenitic stainless steel, duplex stainless steel possess high strength, intergranular corrosion resistance and excellent chloride stress corrosion resistant. and also superior pitting resistance. they take as a stainless steel of nickel saving.
PRODUCT DESCRIPTIONThe alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.