BS EN 2.4889
2015-05-13 14:06:44 Origin： Remark：0 Click：
BS EN material specification EN 2.4889 datasheet, EN 2.4889 Chemical, Ring forging, EN 2.4889 Bar, Wire rod, Sheet - steelmaking, ESR, Blooming, Forging, Rolling, 2.4889 Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS EN 10095 (1999) or By agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION / DATASHEET - BS NiCr28FeSiCe / 2.4889
MATERIAL CATEGORY: Nickel base alloy
MATERIAL SPECIFICATIONS: BS EN 10095 (1999)
CHEMICAL COMPOSITION (WEIGHT %)
C(％): 0.03~0.12
Si(％): 2.50~3.00
Mn(％): ≤1.00
P(％)≤: 0.020
S(％)≤: 0.015
Cr(％): 26.0～29.0
Ni(％): ≥45.0
Al(％): -
Si(％): 2.50~3.00
Mn(％): ≤1.00
P(％)≤: 0.020
S(％)≤: 0.015
Cr(％): 26.0～29.0
Ni(％): ≥45.0
Al(％): -
Other (％): Cu ≤0.30, Fe 21.0 ~ 25.0, Ce 0.03~0.09
MELTING PROCESS
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR).
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
PRODUCT APPLICATION
Heat resisting steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
Heat resisting steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Mr Chen, Mr.Jiang - Email: lh.steel@hotmail.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 4mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Sheet steel via cold rolled: T0.5 - 4mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.