DIN SEW 390 (1991) of Nonmagnetic Steel P900 Ring forging, Round bar, flat bar 1.3816 ESR, hot Forging / Rolling, Heat treated, Cold worked & machined.
MATERIAL DATA SHEET - DIN 1.3816 & P900
MATERIAL CATEGORY: Non-magnetic stainless steel
MATERIAL SPECIFICATIONS - DIN SEW 390 (1991)
Inventory stocklist - Diam.55 ~ 220mm
HS Code for Customs - 72221100 / 72222000
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.10
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％)≤: 0.060
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.5 ~ 20.0
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 17.5 ~ 20.0
Phosphorus, P (％)≤: 0.060
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 17.5 ~ 20.0
Nickel, Ni (％): ≤ 1.00
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.40 ~ 0.70
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.40 ~ 0.70
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 950 ℃
Quenching or solution treatment temperature: 1020 ~ 1120 ℃, water cooled
Tensile strength, σb ≥ /MPa: 750 ~ 950
Yield strength, σ0.2 ≥ /MPa: 480
Elongation, δ ≥ (％): 40.0
Impact at RM temp. Akv ≥/J: 200 (transversal value)
Yield strength, σ0.2 ≥ /MPa: 480
Elongation, δ ≥ (％): 40.0
Impact at RM temp. Akv ≥/J: 200 (transversal value)
PRODUCT DESCRIPTION
The alloy is usually produced by BEF AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution + ageing treatment
The alloy is usually produced by BEF AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution + ageing treatment
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE & DIMENSIONS
Round bar & Disc (diameter): 5.5 to 850mm
Square bar / Flat bar: 10mm to 500mm
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT PROFILE & DIMENSIONS
Round bar & Disc (diameter): 5.5 to 850mm
Square bar / Flat bar: 10mm to 500mm
Forging piece: stepped shafts, other different shapes based on OEM.
Forged retaining ring: OD200 ~ 1220 X ID100 ~ 1000 X H100 ~ 800mm
Forged retaining ring: OD200 ~ 1220 X ID100 ~ 1000 X H100 ~ 800mm
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search：P900
Previous page：AISI/SAE 5046
Last page：40CDV12