S40800
2014-09-29 11:10:59 Origin： Remark：0 Click：
Specifications Ferritic stainless steel S40800 Round bar, Datasheet S40800 Forgings From Melting, ESR & VAR technique, Heat treatment,
TECHNICAL DATA SHEET - Grade UNS S40800
TECHNICAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Ferritic stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.045
Chromium, Cr (％): 11.5 ~ 13.0
Nickle, Ni (％): ≤ 0.08
Molybdenum, Mo (％): -
Titanium, Ti (％): 12 X C ~ 1.10
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, plate, strip and forgings
Tensile strength, σb/MPa: 380
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 25.0
Reduction of area, ф (％): -
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: N
METHOD OF MELTING
The alloy is usually produced by AOD / EAF / VIM, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 470mm
Wire rod (Diameter): 0.50 ~ 13mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
TECHNICAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Ferritic stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.045
Sulfur, S (％)≤: 0.045
Chromium, Cr (％): 11.5 ~ 13.0
Nickle, Ni (％): ≤ 0.08
Molybdenum, Mo (％): -
Titanium, Ti (％): 12 X C ~ 1.10
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, plate, strip and forgings
Tensile strength, σb/MPa: 380
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 25.0
Reduction of area, ф (％): -
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: N
METHOD OF MELTING
The alloy is usually produced by AOD / EAF / VIM, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 470mm
Wire rod (Diameter): 0.50 ~ 13mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
Hot search：S40800
Total list
Monthly rank
- 21ASTM A565 type 616HT
- 18X8CrMnN20-10
- 142Cr11NiMoNbVN
- 13AM-350
- 13X66Cr13
- 13ASTM A693 Gr. XM-16
- 13SUH310
- 13S42035
- 132Cr20Mn9Ni2Si2N
- 12STS321