Z3CND17-12Az Stockist, Z3CND17-12Az Equivalent Steel

Z3CND17-12Az
2017-09-20 13:03:41   Origin:   Remark:0 Click:

Material technical specifications NF A36-209 -1992 Stainless steel Alloy Z3CND17-12Az datasheet, Z3CND17-12Az Chemical compositions, Z3CND17-12Az mechanical properties from Steelmaking, ESR melting, Hot blooming,UT,Z3CND17-12Az Hot forging,Hot rolling,Heat treated, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - NF Z3CND17-12Az

OFFICIAL TEST CERTIFICATE: issued by TUV - SGS BV
MATERIAL CATEGORY: Stainless 
Steel plate for boiler and pressure vessel 
Technical standards: NF A36-209 - 1992
CHEMICAL COMPOSITION (WEIGHT %)
C (%):    ≤ 0.030
Si (%):    ≤ 0.75
Mn (%):  ≤ 2.00
P (%)≤:  0.035
S (%)≤:  0.010
Cr (%):   16.0 ~ 18.0
Mo (%):  2.50 ~ 3.00
Ni (%):    11.0 ~ 13.0
N (%):     0.12 ~ 0.20
MECHANICAL PROPERTIES
Tensile strength,σb/≥ MPa: 580 ~ 780
Yield strength, σ0.2/≥ MPa: 280
Elongation, δ ≥(%): 40.0
Reduction of area, (%): 40.0
Annealed hardness, HB ≤: 250
PRODUCT DESCRIPTION
The
alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment

ADVANTAGED STOCK
High alloy and superalloy for turbine blade
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152
17-4PH/630/1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310
Forms: Bars, Forge piece, Ring, Strip

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers,  E-mail:
lh.steel@hotmail.com

Hot search:Z3CND17-12Az

Previous page:AISI M7 / T13107
Last page:Z3CND17-12-03

Share to: