Z40C14C1
2018-02-14 16:32:28 Origin： Remark：0 Click：
Material technical specifications NF A35-595-992 Stainless steel Z40C14C1 datasheet, Z40C14C1 Chemical compositions, Z40C14C1 mechanical property from Steelmaking,ESR melting,Z40C14C1 Hot blooming, UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - NF Z40C14C1
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel for cutter, tableware
Technical standards: NF A35-575 - 1992
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.36 ~ 0.42
Si (％): ≤ 1.00
MATERIAL CATEGORY: Stainless Steel for cutter, tableware
Technical standards: NF A35-575 - 1992
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.36 ~ 0.42
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 13.0 ~ 14.5
S (％)≤: 0.015
Cr (％): 13.0 ~ 14.5
Mo (％): -
Ni (%): -
MECHANICAL PROPERTIES
Condition: annealed
Tensile strength, TS, σb/≥ MPa: 800
Yield strength, YS, σ0.2/≥ MPa: -
Elongation, EL, δ ≥(％): -
Yield strength, YS, σ0.2/≥ MPa: -
Elongation, EL, δ ≥(％): -
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 245
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
AISI 690 /Refractaloy 26, ASTM A565 Grade 616 /422SS /S42200, Grade 615 /S41800, XM-32 /S64152, PH13-8 /XM-13 /S13800
FV520B /1.4594, PH15-7Mo /632 (S15700), 15-5PH /XM-12 (S15500), 17-4PH /630 /1.4542, 17-7PH /631 (S17700),
851, 961, WB36, D6-AC, D6A. A-286 /ASTM 660, AM-350 /633 (S35000), AM-355 /634 (S35500), Custom 450 /XM-25 (S45000)
1.4980, X22CrMoV12-1 /1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310, X55CrMnN18-4, X50MnCrV20-14, X5MnCrNiN18-13
DIN 1.3964, DIN 1.3974, 23-8N /Nitronic 20,
Forms: Bars, Forge piece, Ring
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter): 0.50mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
- E-mail: lh.steel@hotmail.com
Hot search：Z40C14C1