TECHNICAL DATA SHEET - 1.6358 & AMS 6514

Official test report: issued by TUV - SGS - BV
Material category: 18Ni- 5.0Mo - 9.0Co base maraging stainless steel
Typical chemical elements (mass fraction %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.10
Phosphorus, P (％) ≤: 0.010
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): ≤ 0.50
Nickel, Ni (％): 18.0 ~ 19.0
Molybdenum, Mo (％): 4.60 ~ 5.20
Cobalt, Co (%): 8.30 ~ 9.50
Titanium, Ti (%): 0.60 ~ 0.80
Other (％): Al  0.05 ~ 0.15, Cu ≤ 0.50

MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: after maraging heat treated
Tensile Strength, Rm ≥ MPa: 1070
Yield Strength, Rp0.2 / MPa: 870
Elongation, A5 ≥ (％): 14.0
Reduction of Area, Z ≥ (％): -
Hardness | HRC: 36 max..

PRODUCT DESCRIPTION
AMS6514 alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements. Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment + aged.
Sheet steel via cold rolled: T0.5 - 6mm X W10- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)