FV520B / FV520
2015-02-09 13:45:35 Origin： Remark：0 Click：
FV520B is A Precipitation Hardening Martensitic Stainless steel with an addition of Nb/Cu elements. FV520 Combines High Strength, hardness (up to HRC40), and corrosion resistance. Mechanical properties at RM can be optimized with final age treatment.
TECHNICAL DATASHEET - Grade EN FV520B & FV520
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Precipitation hardening
DENSITY: 7.80kg/dm
MATERIAL SPECIFICATIONS: DIN EN 10088-1
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment / Aged treated.
CHEMICAL COMPOSITION (Mass weight - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): 5.00 ~ 6.50
Molybdenum, Mo (％): 1.20 ~ 2.00
Copper, Cu (％): 1.20 ~ 2.00
MATERIAL CATEGORY: Precipitation hardening
DENSITY: 7.80kg/dm
MATERIAL SPECIFICATIONS: DIN EN 10088-1
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment / Aged treated.
CHEMICAL COMPOSITION (Mass weight - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): 5.00 ~ 6.50
Molybdenum, Mo (％): 1.20 ~ 2.00
Copper, Cu (％): 1.20 ~ 2.00
Niobium, Nb 0.15 ~ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Round bar, flat bar, forgings
Condition: double overaged,1050º C +2 hours 750-850 ºC,+2 hours 750-850 ºC
Proof stress (N/mm²): 800
Tensile strength, σb/MPa: 925 ~ 1035
Yield strength, σ0.2/MPa: 275
Elongation, δ (％): 15.0
Hardness | HB: 277~341
Impact strength, AKv /Min: 40
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut. Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 610mm
Square bar / Flat bar: 3mm to 650mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm, width: 8mm to 800mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Round bar, flat bar, forgings
Condition: double overaged,1050º C +2 hours 750-850 ºC,+2 hours 750-850 ºC
Proof stress (N/mm²): 800
Tensile strength, σb/MPa: 925 ~ 1035
Yield strength, σ0.2/MPa: 275
Elongation, δ (％): 15.0
Hardness | HB: 277~341
Impact strength, AKv /Min: 40
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut. Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 610mm
Square bar / Flat bar: 3mm to 650mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm, width: 8mm to 800mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
Previous page：DIN 25CrMo4
Last page：FV520B / X5CrNiMoCuNb14-5
Total list
Monthly rank
- 261.4418 QT900
- 23GTD 450
- 171.3952
- 17SAE 51410
- 16AISI 630 (17-4PH)
- 15S144
- 15ASTM A182 Gr.F6NM
- 14St T17/13W
- 131.4112
- 13Z5CNU17-4PH