Material technical specifications of KS D3706 stainless steel round bar STS202 datasheet, STS202 Chemical composition, STS 202 Mechanical properties from Remelting, ESR refining, Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - KS D3706 - 2001/2006.
TECHNICAL DATA SHEET - KS D3706 Grade STS202
TECHNICAL SPECIFICATIONS: KS D3706 - 2001/2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 1.00
Mn (％): 7.50 ~ 10.0
Si (％): ≤ 1.00
Mn (％): 7.50 ~ 10.0
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): 4.00 ~ 6.00
S (％) ≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): 4.00 ~ 6.00
Mo (%): -
N (%): ≤ 0.25
TYPICAL MECHANICAL PROPERTY
Tensile strength, σb/ ≥ MPa: 520
Yield strength, σ0.2/ ≥ MPa: 275
Elongation, δ (％) ≥: 40.0
Reduction of area, ф (％) ≥: 45.0
Elongation, δ (％) ≥: 40.0
Reduction of area, ф (％) ≥: 45.0
Hardness ≤ (HBW): 241
HEAT TREATMENT PRACTICE
Condition: solution annealed 1010 ~ 1120 Deg.
Cooling medium: Rapid cool
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 650mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 4 ~ 650 X 4 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Hot search：STS202
Previous page：ASTM A387 type 9
Last page：STS301