FXM-19
2026-08-07 10:51:00 Origin： Remark：0 Click：
ASTM A182 type FXM-19 stock available, FXM-19 technical data sheet round bar FXM-19 Properties flat Bar, plate hot forging & rolled, solution heat treated
TECHNICAL DATA SHEET - FXM-19
TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 21Cr - 12Ni - 5.0Mn austenitic steel
STOCK AVAILABLE: round bar 30 ~ 180 mm
TYPICAL CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.06
Manganese, Mn (％): 4.00 ~ 6.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Nickel, Ni (%): 11.50 ~ 13.5
Chromium, Cr (%): 20.5 ~ 23.5
Molybdenum, Mo (%): 1.50 ~ 3.00
Niobium, Nb (%): 0.10 ~ 0.30
Nitrogen, N (%): 0.20 ~ 0.40
Vanadium, V (%): 0.10 ~ 0.30
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, Rm ≥ MPa: 690
Yield strength, Rp0.2 / MPa: 380
Elongation, A5 ≥ (％): 35.0
Reduction of area, Z ≥ (％): 55.0
Hardness via heat treatment / HB: -
HEAT TREATMENT PRACTICE
Condition: solution annealing (+AT)
Cooling medium: water or oil cooling
Tempering temperature: 1040 Deg.C
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar & rod & disc (diameter): 6.0 ~ 500 mm
Square bar & flat bar: 10 to 600 mm
Length: random length or based on the customer's special requirement.
Heavy / middle plate: T6 ~ 400 X W60 ~ 1000 X L1000 ~ 3500 mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry or help, pleased to E-mail our resident team of qualified production engineers - Email: sales@ccsteels.com.