15-15LC Stockist, 15-15LC Equivalent Datasheet

15-15LC
2022-12-31 16:06:10   Origin:   Remark:0 Click:

15-15LC Modified stainless is nonmagnetic, austenitic Mn-Cr-steel with a high nitrogen content, P530 Round bar, flat bar, and plate ESR refined, Hot forging/rolling, 100% Ultrasonic flaw detection test, Cold working or Machined.

RAW MATERIAL SPECIFICATIONS - Non-magnetic Stainless 15-15LC


MATERIAL CATEGORY - Nonmagnetic, austenitic Mn-Cr-steel with a high nitrogen content.
MATERIAL SPECIFICATIONS - DIN SEW 390 (1991), Equivalent to Grade P530
OFFICIAL TEST CERTIFICATE - issued by TUV - SGSBV
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (%):  ≤ 0.05
Silicon, Si (%):  ≤ 1.00
Manganese, Mn (%):  15.0 ~ 19.0
Phosphorus, P (%)≤:  0.050
Sulfur, S (%)≤:  0.030
Chromium, Cr (%):  16.0 ~ 21.0
Nickel, Ni (%):  ≤ 3.00
Molybdenum, Mo (%):  0.50 ~ 3.00
Nitrogen, N (%):  0.20 ~ 0.80
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 950℃
Quenching or solution treatment temperature: 1020~1120℃, water / oil cooled
Tensile strength,  σb≥ /MPa: 900
Yield strength,  σ0.2 ≥/MPa: 760
Elongation, δ≥(%): 35.0
Impact Akv ≥/J: 150
Hardness: HB 285 min.
PRODUCT DESCRIPTION
The
alloy is usually produced by IFF + ESR /AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
PROFILE AND DIMENSIONS AVAILABLE
Round bar (Diameter): 5.5 to 450mm
Square bar / Flat bar: 10mm to 300mm
Retainer ring: OD1200 X ID 30mm
Length: Fixed length or random length or based on the customer's special requirement.
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:
sales@ccsteels.com

Hot search:15-15LC

Previous page:AMS 5666 & N06625 Round bar, Sheet, Plate
Last page:最后一页

Share to: