Corrosion resisting steel AMS 5616
2026-09-02 14:36:28 Origin： Remark：0 Click：
Martensitic stainless steel high tensile steel AMS 5616 round bar, S41800 flat bar, forging stock heat-treatable corrosion-resistant steel
TECHNICAL DATA SHEET - AMS 5616
Material category: 13Cr - 2.0Ni - 3.0W - 0.18C martensitic stainless steel
Technical standards: AMS 5616M
Technical standards: AMS 5616M
Stock in hand: round bar, steel strip 0.74 x 200 mm
Typical chemical compositions ( mass weight - %)
SHAPES & DIMENSIONS
Round bar, disc: 6.0 to 800 mm
Square bar, flat bar: 10 to 500 mm
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Carbon, C (％): 0.15 ~ 0.20
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): 1.80 ~ 2.20
Molybdenum, Mo (％): ≤ 0.50
Tungsten, W (％): 2.50 ~ 3.50
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): 1.80 ~ 2.20
Molybdenum, Mo (％): ≤ 0.50
Tungsten, W (％): 2.50 ~ 3.50
Aluminium, Al (%): ≤ 0.15
Copper, Cu (%): ≤ 0.50
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb ≥ MPa: 1034
Yield strength, σ0.2 ≥ MPa: -
Yield strength, σ0.2 ≥ MPa: -
Elongation, A5 ≥ (％): 10.0
Reduction of area, Z ≥ (％): -
Hardness, HB: ≤ 311 (annealed condition)
Reduction of area, Z ≥ (％): -
Hardness, HB: ≤ 311 (annealed condition)
Condition of heat treatment: HT 981℃ ~ 1080℃ air or oil cooled, ≥ 620℃ X 2H, two times tempered
Tensile strength, σb ≥ MPa: 965
Yield strength, σ0.2 ≥ MPa: 760
Yield strength, σ0.2 ≥ MPa: 760
Elongation, δ5 ≥ (％): 15.0
Reduction of area, ф ≥ (％): 45.0
Hardness, HBW: 302 ~ 352
Reduction of area, ф ≥ (％): 45.0
Hardness, HBW: 302 ~ 352
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
SHAPES & DIMENSIONS
Round bar, disc: 6.0 to 800 mm
Square bar, flat bar: 10 to 500 mm
Length: random length or based on the customer's special requirement.
Other different shapes based on OEM.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers - E-mail: sales@ccsteels.com
Further, please also check the materials in stock available:
Raw material - steels of blade for steam turbine
XM-25, S45000, GD450, C450
403 ESR, GB8732 type 12Cr12Mo, 10705BA/BB/BC
AISI 616, 422, 1.4935, X20CrMoWV12-1, 10705BU
B50A365B, 403Cb+, 1.4913, X19CrMoVNbN11-1
17-4PH, 630, 1.4542, X5CrNiCuNb16-4, 10705GU/GV/GW
M-152, S64152, 1.4938, X12CrNiMoV12-3, S151D
FV520B, S143, 1.4594, X4CrNiCuMo14-5
X22CrMoV12-1, 1.4923
13Х11Н2B2MФ, AE961W
15-5PH, XM-12, S15500
A286, AISI 660, S66286
10705MBU, 10705AJ
Non-magnetic steel:
1.3813, X40MnCrN19, 1.3816, X8MnCrN18-18
1.3817, X40MnCr18, 1.3818, X55MnCrN18-4
Hot search：
Previous page：Heat resisting steel 10Cr9MoW2VNbBN
Last page：最后一页
Total list
Monthly rank
- 16X10CrNiW17-13-3
- 15FV535
- 14S16800
- 13E-Z6NCT25
- 12ASTM A565 type 616
- 12S17400
- 12X12CrNi17-7
- 12ASTM A182 Grade F6b
- 12S131
- 11Uranus 50 / S32404