Specifications X14CrMoS17 Datasheet, X14CrMoS17 Chemical, X14CrMoS17 Property Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DATA SHEET - DIN X14CrMoS17
MATERIAL CATEGORY - Ferritic type
MATERIAL SPECIFICATIONS - DIN 17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10 ~ 0.17
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.15 ~ 0.35
Cr (％): 15.5 ~ 17.5
Ni (％): -
Mo (％): 0.20 ~ 0.60
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.15 ~ 0.35
Cr (％): 15.5 ~ 17.5
Ni (％): -
Mo (％): 0.20 ~ 0.60
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: annealed
Thickness/mm: -
Thickness/mm: -
σb/MPa: 730 max.
σ0.2≥/MPa: 300
δ5≥(％): 16
σ0.2≥/MPa: 300
δ5≥(％): 16
ψ≥(％): -
Akv≥/J: -
Hardness HBS30: 220
Akv≥/J: -
Hardness HBS30: 220
Condition: HT
Thickness/mm: 60/160
Thickness/mm: 60/160
σb/MPa: 650 ~ 850
σ0.2≥/MPa: 500
δ5≥(％): 12/10
δ5≥(％): 12/10
ψ≥(％): 50
Akv≥/J: -
Hardness HBW30: -
Akv≥/J: -
Hardness HBW30: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：X14CrMoS17