X5CrNi18-10
2025-07-20 08:12:00 Origin： Remark：0 Click：
Specifications X5CrNi18-10 Round bar, Wire rod, plate, Properties from steelmaking, Hot forging, Hot rolling, Heat treatment, Cold working.
TECHNICAL DATA SHEET - DIN X5CrNi18-10
MATERIAL CATEGORY: Austenitic corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF / followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / EAF / followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 8.00 ~ 10.5
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.11
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 8.00 ~ 10.5
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.11
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution treatment
Thickness / mm: 160
Thickness / mm: 160
Tensile strength, σb / MPa: 500 ~ 700
Yield strength, σ0.2 ≥ MPa: 190
Elongation, δ5 ≥ (％): 45/35
Elongation, δ5 ≥ (％): 45/35
Reduction of area, ψ ≥ (％): 60
Impact strength, Akv ≥ J: 100/60
40Hardness HBS30: 215max
Impact strength, Akv ≥ J: 100/60
40Hardness HBS30: 215max
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1000~1100 air/water cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: solution
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃ | 100: 155
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃ | 200: 127
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃ | 200: 127
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃ | 300: 110
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃ | 400: 98
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃ | 400: 98
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃ | 500: 92
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nut, Pressure vessel parts.
Bolt and nut, Pressure vessel parts.
PRODUCT PROFILE & DIMENSIONS
Round bar / rod (diameter): 5.5mm to 600mm
Square bar / flat bar: 3mm to 800mm
Round bar / rod (diameter): 5.5mm to 600mm
Square bar / flat bar: 3mm to 800mm
Length: random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
Hot search：X5CrNi18-10
Total list
Monthly rank
- 89ASTM A565 type 616HT
- 29N06102
- 28Z15CN17-03
- 2410705BU
- 22X11CrMo12-1
- 21Z10CNT18-11
- 21X35CrMo17
- 18EN 57
- 16X66Cr13
- 15X2Cr11 / 1.4003