ASTM B408 N08810
2016-09-27 11:51:46   Origin:   Remark:0 Click:

Standard specifications for Nickel - Iron - Chromium alloy rod and bar N08810 data sheet, N08810 Chemical compositions, N08810 mechanical properties from Steel making, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. Technical specification ASTM B408 - 2006.
TECHNICAL SPECIFICATION - ASTM B408 GRADE N08810

TECHNICAL SPECIFICATION: ASTM B408 - 2006
OFFICIAL TEST CERTIFICATE: issued by
TUV - SGSBV

MATERIAL CATEGORY:  Nickel - Iron - Chromium alloy rod and bar
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     0.05 ~ 0.10
Si (%):     ≤ 1.00
Mn (%):   ≤ 1.50
P (%) ≤:  0.045
S (%) ≤:  0.015
Cr (%):    19.0 ~ 23.0
Ni (%):     30.0 ~ 35.0
Mo (%):   -
Ti (%):     0.15 ~ 0.60
Cu (%):    ≤ 0.75
Al (%):     0.15 ~ 0.60
N (%):      -
Nb (%):    -
Co (%):    -
W (%):     -
Fe (%):     39.5 Min.
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Form: round bar
Condition: cold worked and hot worked, annealed, at 1121 Deg. min.
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 170
Elongation, δ ≥(%): 30.0
Reduction of area, ф ≥ (%): -
Hardness | HRC: -
Service temperature: above 593 Deg.
TYPICAL APPLICATIONS

Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Gas turbine
Turbine blade
Fuel nozzle
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.

FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email:
lh.steel@hotmail.com    

Hot search:ASTM B408 N08810

Previous page:ASTM B805 N09925
Last page:Incoloy 800H / N08810

Share to: