C (％): ≤ 0.030
Si (％): 4.00 ~ 6.00
Mn (％): ≤ 1.50
P (％)≤: 0.025
Cr (％): 19.0 ~ 22.0
Co (%): -
Al (%): -
Ti (%): -
Reduction of area, ф ≥ (％): -
Hardness via annealing | HBW: -
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
FORMS AND SHAPES
Round bar (Diameter): 5.50 ~ 550mm
Square bar / Flat bar: 3 ~ 450mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.