1.4923
2014-09-12 10:28:10   Origin:   Remark:0 Click:

Description 1.4923 Suppliers, Round bar 1.4923 Stocklist, Inventory 1.4923 Ring machined from Melting, ESR & VAR processing technique, Blooming, Hot forging & rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test,
TECHNICAL DATA SHEET - Grade W-Nr 1.4923

MATERIAL CATEGORY - High temperature high strength steel and superalloy 
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480, DIN EN 10302, 10296, 10095
CHEMICAL COMPOSITION (Mass weight - %)
C (%):     0.18 ~ 0.24
Si (%):    0.18 ~ 0.24
Mn (%):   0.40 ~ 0.90
P (%)≤:   0.025
S (%)≤:   0.015
Cr (%):    11.0 ~ 12.5
Ni (%):    0.30 ~ 0.80
Mo (%):   0.80 ~ 1.20
V (%):     0.25 ~ 0.35
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃: 1100~850
Heat treatment temperature /℃ | annealing: 750~780    
Heat treatment temperature /℃ | quenching or solution: 1035 ~ 1065 air / oil 
Heat treatment temperature /℃ | tempering: 700~750
Heat treatment temperature /℃ | ageing:   630~750
Condition: heat treatment
Mechanical property under room temperature |σb/MPa: 800 ~ 950                  
Mechanical property under room temperature  |σs≥/MPa:  600    
Mechanical property under room temperature |δ5≥(%): 14      
Mechanical property under room temperature |Akv(DVM):  34       
Heat stability temperature/℃:   580
Non-scale temperature in air /℃:   600
TYPICAL APPLICATIONS 
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR or VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
AVAILABLE SHAPES
Round bar / flat bar / square bar / forgings / plate  
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring / pipe casing / discs / shaft
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Plate / Sheet steel / Steel strip: 0.5mm to 200mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.