Inconel 604
2025-10-07 06:10:00 Origin： Remark：0 Click：
Technical specifications Inconel 604 peeled bright round bar, sheet, plate ESR & VAR technique, hot bloomed, forged, rolled, heat treated
TECHNICAL DATA SHEET - Inconel 604
Official test report: issued by TUV - SGS - BV
Material category: Cr-Ni base Superalloy
Typical chemical elements (mass fraction %)
Carbon, C (％): 0.020 ~ 0.060
Carbon, C (％): 0.020 ~ 0.060
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％): ≤ 0.025
Phosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.015
Chromium, Cr (％): 14.0 ~ 17.0
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (％): remainder
Molybdenum, Mo (％): -
Cobalt, Co (%): -
Cobalt, Co (%): -
Tungsten, W (%): -
Aluminum, Al (%): -
Aluminum, Al (%): -
Copper, Cu (%): ≤ 0.35
Niobium, Nb (%): 1.75 ~ 3.00
Ferrum, Fe (% ): 6.20 ~ 9.00
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb ≥ MPa: 550
Yield strength, σ0.2 / MPa: 315
Elongation, δ5 ≥ (％): 35.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND DIMENSIONS
Round bar (diameter): 6.0 ~ 450mm
Square bar / flat bar: 8 ~ 600mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND DIMENSIONS
Round bar (diameter): 6.0 ~ 450mm
Square bar / flat bar: 8 ~ 600mm
Wire rod (diameter): 0.50 ~ 13mm
Steel strip via cold rolled: T0.1 ~ 3.0 X W5 ~ 650 X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 ~ 3.0 X W5 ~ 650 X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.