Datatsheet S41425 Chemical, S41425 Specifications, S41425 Properties from Steelmaking, ESR melted, Hot Blooming, Hot forging & Rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3
MATERIAL DATA SHEET - UNS S41425
HSN CODE - 72221100 / 72222000
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment / QT
AVAILABILITY
Round bar / flat bar / strip / plate / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / strip / plate / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 12.0 ~ 15.0
Mo (％): 1.50 ~ 2.00
Ni (％): 4.00 ~ 7.00
N (&): 0.06 ~ 0.12
Cu (％): ≤ 0.30
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 12.0 ~ 15.0
Mo (％): 1.50 ~ 2.00
Ni (％): 4.00 ~ 7.00
N (&): 0.06 ~ 0.12
Cu (％): ≤ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: 925~981℃ air cooling, 570℃ x 1h tempering
Tensile strength, σb/MPa: 825
Yield strength, σ0.2/MPa: 655
Elongation, δ (％): 15.0
Yield strength, σ0.2/MPa: 655
Elongation, δ (％): 15.0
Reduction of area, ψ (％)≥: -
Impact, Akv ≥/J: -
Hardness: HBW: 321 Max.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.50mm to 550mm
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.50mm to 550mm
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mai: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, E-mai: sales@ccsteels.com.
Hot search：S41425
Previous page：ASTM 403Cb
Last page：S42300
Total list
Monthly rank
- 50FSX-414
- 16Aquamet 22
- 1510705BU
- 15AMS 5221
- 13Carpenter 20 Mo 4
- 12X12CrNiMoV12-2
- 11Inconel 610
- 10AMS 5354
- 9Incoloy 840
- 8Aquamet 17