S41425
2014-10-14 09:52:09 Origin： Remark：0 Click：
ASTM A959 (2004) / ASTM A632 of Grade S41425 Round bar, flat bar, ESR melted, Blooming, Hot forging & Rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or machined.
TECHNICAL DATA SHEET - Grade UNS S41425
MATERIAL CATEGORY - Martensite type - 13Cr-5Ni-2Mo
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / EAF / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 12.0 ~ 15.0
Molybdenum, Mo (％): 1.50 ~ 2.00
Nickel, Ni (％): 4.00 ~ 7.00
Nitrogen, N (&): 0.06 ~ 0.12
Copper, Cu (％): ≤ 0.30
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 12.0 ~ 15.0
Molybdenum, Mo (％): 1.50 ~ 2.00
Nickel, Ni (％): 4.00 ~ 7.00
Nitrogen, N (&): 0.06 ~ 0.12
Copper, Cu (％): ≤ 0.30
MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT)
Condition of heat treatment: 925~981℃ air cooling, 570℃ x 1h tempering
Tensile strength, σb/MPa: 825
Yield strength, σ0.2/MPa: 655
Elongation, δ (％): 15.0
Yield strength, σ0.2/MPa: 655
Elongation, δ (％): 15.0
Reduction of area, ψ (％)≥: -
Impact, Akv ≥/J: -
Hardness | HRB(HRC): ≤321
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE