Specifications X8CrNiMoAl15-7-2 stainless, X8CrNiMoAl15-7-2 Chemical, X8CrNiMoAl15-7-2 Wire rod properties from steelmaking,forging,rolling,heat treatment,cold working.We also possess advanced precision machining equipments for further processing.
TECHNICAL DATA SHEET - DIN X8CrNiMoAl15-7-2
MATERIAL CATEGORY: Common alloy steel - Hardening corrosion resisting steels
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Maraging steels are iron-nickel alloys with absence of carbon and have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness characteristics and weldability. Typically, these alloys are used in aerospace applications, machinery and tooling and ordnance components and fasteners.
MATERIAL SPECIFICATIONS
DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5(2005)
DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5(2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.10
Si (％): ≤ 0.70
Mn (％): ≤ 1.20
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 14.0 ~ 16.0
Ni (％): 6.50 ~ 7.80
Mo (％): 2.00 ~ 3.00
Al (％): 0.70～1.50
Si (％): ≤ 0.70
Mn (％): ≤ 1.20
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 14.0 ~ 16.0
Ni (％): 6.50 ~ 7.80
Mo (％): 2.00 ~ 3.00
Al (％): 0.70～1.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: annealed
Thickness/mm: -
Tensile strength, Rm σb/MPa: 1100 max.
Yield strength, Re σ0.2≥/MPa: -
Elongation, δ5≥(％): 20.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: -
Yield strength, Re σ0.2≥/MPa: -
Elongation, δ5≥(％): 20.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: -
Hardness HBS30: -
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Heat treatment temperature and cooling methods|annealing: 945~965 rapid cooling
Heat treatment temperature and cooling methods|quenching: 500~520 aging,air cooling
Heat treatment temperature and cooling methods|tempering: -
Condition: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|100: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|200: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|300: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|400: -
High temperature yield strength σ0.2/MPa≥/MPa，at below temp/℃|500: -
TYPICAL APPLICATIONS
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：X8CrNiMoAl15-7-2
Previous page：1.4529 / X1NiCrMoCuN25-20-7
Last page：1.4532