1.4713
2026-02-10 11:01:00 Origin： Remark：0 Click：
EN 10095 material specification 1.4713 peeled round bar, milled flat bar, plate and forgings 1.4713 ESR, hot forged, rolled, heat treated, cold worked
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - DIN 1.4713
Material category - heat resisting steel and Cr7.0 - Al 0.75 base steel
Material specifications - EN 10095 (1999)
Typical chemical compositions (mass fraction %)
Carbon, C (％): ≤ 0.12
Silicon, Si (％): 0.50 ~ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 6.00 ~ 8.00
Nickel, Ni (％): -
Aluminum, Al (％): 0.50 ~ 1.00
Silicon, Si (％): 0.50 ~ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 6.00 ~ 8.00
Nickel, Ni (％): -
Aluminum, Al (％): 0.50 ~ 1.00
HEAT TREATMENT AND MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Hardness ≤ HBW: 192
Hot working temperature /℃: 1100~800
Heat treatment temperature /℃: 780~840
Heat treatment temperature /℃: 780~840
Heat treatment temperature /℃|solution treatment: -
Condition: + annealed
Tensile strength, Rm ≥ MPa: 420～620
Yield strength, Rp0.2 ≥ MPa: 220
Elongation, A5 (％) ≥: 20.0
Condition: + annealed
Tensile strength, Rm ≥ MPa: 420～620
Yield strength, Rp0.2 ≥ MPa: 220
Elongation, A5 (％) ≥: 20.0
MELTING PROCESS
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
FORMS AND DIMENSIONS
Round bar / disc (diameter1): 6.0 to 850 mm
Square bar / flat bar: 8 to 600 mm
Length: random length or based on the customer's special requirement.
Round bar / disc (diameter1): 6.0 to 850 mm
Square bar / flat bar: 8 to 600 mm
Length: random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 ~ 300 X W60 ~ 1000 X L1000 ~ 12000 mm
Sheet steel via cold rolled: T0.5 - 4mm X W100 - 750mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Sheet steel via cold rolled: T0.5 - 4mm X W100 - 750mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, other different shapes based on OEM.