Specifications 1.4713 datasheet, 1.4713 Chemical, Ring forging 1.4713 Bar, Wire rod, Sheet - steelmaking, ESR, Blooming, Forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Technical Standards - BS EN 10095 (1999) or By agreement.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - EN 1.4713
MATERIAL CATEGORY: Heat resisting steel and Nickel base alloy
MATERIAL SPECIFICATIONS: BS EN 10095 (1999)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.12
Si (％): 0.50 ~ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 6.00 ~ 8.00
Ni (％): -
Al (％): 0.50 ~ 1.00
Si (％): 0.50 ~ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 6.00 ~ 8.00
Ni (％): -
Al (％): 0.50 ~ 1.00
HEAT TREATMENT AND MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Hardness ≤HBW: 192
Hot working temperature /℃: 1100~800
Heat treatment temperature /℃: 780~840
Heat treatment temperature /℃: 780~840
Heat treatment temperature /℃|solution treatment: -
|Condition: annealed
Tensile strength, |σb≥/MPa: 420～620
Yield strength, |σ0.2≥/MPa: 220
Elongation, |δ5(％)≥: 20.0
|Condition: annealed
Tensile strength, |σb≥/MPa: 420～620
Yield strength, |σ0.2≥/MPa: 220
Elongation, |δ5(％)≥: 20.0
MELTING PROCESS
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR).
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
PRODUCT APPLICATION
Heat resisting steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
Heat resisting steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter1): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 300mm X W60 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 4mm X W100 - 750mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Sheet steel via cold rolled: T0.5 - 4mm X W100 - 750mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Previous page：X10CrAlSi7
Last page：BS X10CrAlSi13