DIN EN 10302 specifications austenitic creep-resisting steel X6NiCrTiMoVB25-15-2 round bar, wire rod, 1.4980 forgings, heat treated, ultrasonic test, cold worked, machined.
TECHNICAL DATA SHEET - X6NiCrTiMoVB25-15-2
MATERIAL CATEGORY: austenitic creep-resisting steels
FEATURES AND CLASSIFICATIONS
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
Heat-resistant steel means one type of steel possesses inoxidizability, enough high-temperature strength and excellent heat-resistant quality under high temperature. Heat resistant steel is divided into oxidation resistant steel and refractory steel according to its performance. Further into Austenitic heat-resistant steel, Martensitic heat-resistant steel, Ferritic heat-resistant steel and Pearlitic heat-resistant steel according to its normalizing.
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095, EN 10088-1 (2005)
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.03 ~ 0.08
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 1.00 ~ 2.00
Phosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.015
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 1.00 ~ 2.00
Phosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.015
Nitrogen, N (%): -
Aluminum, Al (%): ≤ 0.35
Chromium, Cr (％): 13.5 ~ 16.0
Molybdenum, Mo (％): 1.00 ~ 1.50
Molybdenum, Mo (％): 1.00 ~ 1.50
Niobium, Nb (%): -
Nickel, Ni (％): 24.0 ~ 27.0
Titanium, Ti (%): 1.90 ~ 2.30
Vanadium, V (%): 0.10 ~ 0.50
Tungsten, W (%): -
Boron, B (％): 0.0030 ~ 0.010
Boron, B (％): 0.0030 ~ 0.010
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Condition: solution treatment
Tensile strength, σb / MPa: 930 ~ 1180
Tensile strength, σb / MPa: 930 ~ 1180
Yield strength, σs ≥ MPa: 635
Elongation, δ5 ≥ (％): 12.0
Elongation, δ5 ≥ (％): 12.0
Non-scale temperature in Air ℃: 820
APPLICATION FIELD
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in vacuum induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in vacuum induction furnace. For higher quality,it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：X6NiCrTiMoVB25-15-2
Previous page：1.4971
Last page：X5NiCrTi26-15
Total list
Monthly rank
- 21ASTM A565 type 616HT
- 18X8CrMnN20-10
- 142Cr11NiMoNbVN
- 13AM-350
- 13X66Cr13
- 13ASTM A693 Gr. XM-16
- 13SUH310
- 13S42035
- 132Cr20Mn9Ni2Si2N
- 12STS321