X40MnCrN19
2015-03-02 09:52:14 Origin： Remark：0 Click：
X40MnCrN19 Non-magnetic alloy steel, 1.3813 Round bar, flat bar, plate, forged ring. Hot forging & Rolling, Heat treated, cold worked, Technical standards - DIN SEW 390 (1991).
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
NON-MAGNETIC ALLOY DATASHEET - DIN X40MnCrN19
MATERIAL CATEGORY - Non-magnetic stainless steel and alloy
MATERIAL SPECIFICATIONS - DIN SEW 390 (1991)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.30 ~ 0.50
Silicon, Si (％): ≤ 0.80
Manganese, Mn (％): 18.0 ~ 20.0
Phosphorus, P (％)≤: 0.100
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 3.00 ~ 5.00
Silicon, Si (％): ≤ 0.80
Manganese, Mn (％): 18.0 ~ 20.0
Phosphorus, P (％)≤: 0.100
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 3.00 ~ 5.00
Nickel, Ni (％): -
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.08 ~ 0.12
Molybdenum, Mo (％): -
Nitrogen, N (％): 0.08 ~ 0.12
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1050 ~ 850℃
Quenching or solution treatment temperature: 1000~1050℃
Tensile strength, σb≥ /MPa: 740~930
Yield strength, σ0.2 ≥/MPa: 295
Elongation, δ ≥(％): 45.0
Impact strength, Akv ≥/J: 124
Yield strength, σ0.2 ≥/MPa: 295
Elongation, δ ≥(％): 45.0
Impact strength, Akv ≥/J: 124
TYPICAL APPLICATIONS
High-voltage electrical apparatus, bolts and nuts.
Transformer tank, Generator ring, Preparation equipments, Electronics.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
FORMS & DIMENSIONS AVAILABLE
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 10mm to 400mm
Heavy/middle plate via hot rolled: T10 - 400mm X W20 - 450mm X L1000 - 4000mm
Square bar / Flat bar: 10mm to 400mm
Heavy/middle plate via hot rolled: T10 - 400mm X W20 - 450mm X L1000 - 4000mm
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email our resident team of qualified production engineers. E-mail: sales@ccsteels.com
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search：X40MnCrN19