1.3805
2026-02-13 09:09:00 Origin： Remark：0 Click：
DIN SEW 390 (1991) material specifications austenitic steel 1.3805 peeled round bar, flat bar, bolts and nuts 1.3805 retaining ring, rolled plate steelmaking, 1040℃ heat treated
TECHNICAL DATA SHEET - 1.3805
Official test certificate: issued by TUV - SGS - BV
Technical specifications: DIN SEW 390 (1991)
Typical chemical compositions (mass weight %)
Carbon, C (％): 0.30 ~ 0.40
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 19.0 ~ 22.0
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): -
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 19.0 ~ 22.0
Phosphorus, P (％) ≤: 0.060
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): -
Nickle, Ni (％): ≤ 1.00
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.10
Molybdenum, Mo (％): -
Nitrogen, N (％): ≤ 0.10
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150~950℃
Quenching or solution treatment temperature: 1000 ~ 1100℃
Tensle strength, σb ≥ MPa: 650~900
Yield strength, σ0.2 ≥ MPa: 240
Reduction of area, δ5 ≥ (％): 22.0
Impact, Akv ≥ J: 55 (transversal value)
Yield strength, σ0.2 ≥ MPa: 240
Reduction of area, δ5 ≥ (％): 22.0
Impact, Akv ≥ J: 55 (transversal value)
PRODUCT DESCRIPTION
The alloy 1.3805 is usually produced by BEF / AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / quenched and tempered
The alloy 1.3805 is usually produced by BEF / AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / quenched and tempered
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE AND DIMENSIONS AVAILABLE
Round bar & disc (diameter): 6.0 to 710 mm
Square bar / flat bar: 10 to 600 mm
Round bar & disc (diameter): 6.0 to 710 mm
Square bar / flat bar: 10 to 600 mm
Length: random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T6 ~ 400 X W60 ~ 1000 X L1000 ~ 5000 mm
Forging piece: different shapes based on OEM.
Forging piece: different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：1.3805
Previous page：X35Mn21
Last page：X40MnCrN19
Total list
Monthly rank
- 21ASTM A565 type 616HT
- 18X8CrMnN20-10
- 142Cr11NiMoNbVN
- 13AM-350
- 13X66Cr13
- 13ASTM A693 Gr. XM-16
- 13SUH310
- 13S42035
- 132Cr20Mn9Ni2Si2N
- 12STS321