EN 1.4436
2015-04-08 08:37:55 Origin： Remark：0 Click：
EN 10083-3 Austenitic stainless steel material specification EN 1.4436 Sheet - steelmaking, 1.4436 Forging, Hot Rolling, Heat treatment, Straightened
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - BS X3CrNiMo17-13-3 & 1.4436
MATERIAL CATEGORY: Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE: Austenitic series
MATERIAL SPECIFICATIONS: BS EN 10083-3 (2005)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.050
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 16.5～18.5
Nickel, Ni (％): 10.5～13.0
Molybdenum, Mo (％): 2.50～3.00
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.045
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 16.5～18.5
Nickel, Ni (％): 10.5～13.0
Molybdenum, Mo (％): 2.50～3.00
Nitrogen, N (％): ≤ 0.11
MECHANICAL PROPERTIES AND INTERGRANULAR CORROSION RESISTANT TENDENCY VIA SOLUTION TREATMENT
Thickness Diameter (d)/≤mm: 160
Hardness HBS: 215
Yield strength σ0.2≥/MPa: 200
Tensile strength σb/MPa: 500～700
Yield strength σ0.2≥/MPa: 200
Tensile strength σb/MPa: 500～700
Elongation δ(longitudinal )≥(％): 40
Elongation δ(transversal )≥(％): -
Impact absorbing energy Akv≥/J|longitudinal: 100
Impact absorbing energy Akv≥/J|transversal: -
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: No
Impact absorbing energy Akv≥/J|transversal: -
Intergranular corrosion resistance tendency | condition of delivery: Yes
Intergranular corrosion resistance tendency | condition of welding: No
Thickness Diameter (d)/≤mm: 160<d≤250
Hardness HBS: 215
Yield strength σ0.2≥/MPa: 200
Tensile strength σb/MPa: 500～700
Elongation δ(longitudinal )≥(％): -
Yield strength σ0.2≥/MPa: 200
Tensile strength σb/MPa: 500～700
Elongation δ(longitudinal )≥(％): -
Elongation δ(transversal )≥(％): 30
Impact absorbing energy Akv≥/J|longitudinal: -
Impact absorbing energy Akv≥/J|transversal: 60
Intergranular corrosion resistance tendency | condition of delivery: YesImpact absorbing energy Akv≥/J|transversal: 60
Intergranular corrosion resistance tendency | condition of welding: No
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (Diameter1): 5.50mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Disc (Diameter1): 5.50mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Forging piece: stepped shafts, and other different shapes based on OEM.