Technical standards BS EN 10095 (1999) heat resisting steel 1.4724 peeled round bar, flat bar, rod, plate ESR, hot bloomed, forged, rolled, heat treated
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - EN 1.4724
Material category - heat resisting steel 13.%Cr - 0.95%Al - 1.05%Si base steel
Technical specifications - BS EN 10095 (1999)
Typical chemical compositions (mass fraction %)
Carbon, C (％): ≤ 0.12
Silicon, Si (％): 0.70 ~ 1.40
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％): ≤ 0.040
Sulfur, S (％): ≤ 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Aluminum, Al (％): 0.70 ~ 1.20
Silicon, Si (％): 0.70 ~ 1.40
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％): ≤ 0.040
Sulfur, S (％): ≤ 0.015
Chromium, Cr (％): 12.0 ~ 14.0
Nickel, Ni (％): -
Aluminum, Al (％): 0.70 ~ 1.20
HEAT TREATMENT AND MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Hardness ≤ HBW: 192
Hot working temperature / ℃: 1100~800
Heat treatment temperature / ℃: 800~860
Heat treatment temperature / ℃: 800~860
Heat treatment temperature / ℃ | solution treatment: -
|Condition: + annealed
Tensile strength, σb ≥ MPa: 450～650
Yield strength, Rp0.2 ≥ MPa: 250
Elongation, A5 (％) ≥: 15.0
|Condition: + annealed
Tensile strength, σb ≥ MPa: 450～650
Yield strength, Rp0.2 ≥ MPa: 250
Elongation, A5 (％) ≥: 15.0
MELTING PROCESS
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in electric arc furnace (EAF ) or induction furnace + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
PRODUCT APPLICATION
Heat resisting steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Heat resisting steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
PROFILE AND DIMENSIONS
Round bar / rod / disc (diameter1): 6.0 to 610 mm
Square bar / flat bar: 10 to 600 mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / rod / disc (diameter1): 6.0 to 610 mm
Square bar / flat bar: 10 to 600 mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T6 ~ 400 X W80 ~ 1000 X L1000 ~ 12000 mm
Sheet steel via cold rolled: T0.5 ~ 4 X W15 ~ 1000 X L1000 ~ 2000 mm
Steel strip via cold rolled: T0.1 ~ 3 X W10 ~ 200 X L mm (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 ~ 4 X W15 ~ 1000 X L1000 ~ 2000 mm
Steel strip via cold rolled: T0.1 ~ 3 X W10 ~ 200 X L mm (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Previous page：BS X10CrAlSi13
Last page：BS X10CrAlSi18
Total list
Monthly rank
- 51S16800
- 43X35CrMo17
- 23FV535
- 22ASTM A538 / AMS 6514
- 21Magnadur 601
- 20X22CrMoV12-1
- 16S165M / S165
- 1618Cr12MoVNbN
- 1510705BA
- 15Z8CND17-04