Technical specifications of DIN X6CrMo15 Martensitic stainless steel, X6CrMo15 Round bar, Flat bar, and ESR melted, Hot forging, Heat treatment
TECHNICAL DATA SHEET - Grade X6CrMo15
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 14.0 ~ 16.0
Nickel, Ni (％): ≤ 0.50
Molybdenum, Mo (％): 1.50 ~ 2.00
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 14.0 ~ 16.0
Nickel, Ni (％): ≤ 0.50
Molybdenum, Mo (％): 1.50 ~ 2.00
Nitrogen, N (%): ≤ 0.05
Aluminum, Al (%): ≤ 0.05
MECHANICAL PROPERTIES AT ROOM.
Tensile strength, σb ≥ MPa: -
Yield strength, σ0.2 ≥ MPa: -
Elongation, δ ≥ (％): -
Elongation, δ ≥ (％): -
Reduction of area, ф ≥ (％): -
Hardness | HRB: 250 Max.
APPLICATION FIELD
Tall oil distillation columns and equipments, Food processing equipments.
Hydrometallurgy, heat exchangers, Oil and gas production equipments.
Pulp mill bleach systems, Seawater handling equipments.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：X6CrMo15