S30615 Suppliers, S30615 Forging Bar plate machined, S30615 Alloy Exporters, S30615 Technical specifications From Melting, ESR & VAR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
MATERIAL DATA SHEET - UNS S30615
MATERIAL CATEGORY: 18Cr-15Ni-3Si-Al Austenitic steel
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / BEF + AOD / VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by EAF / BEF + AOD / VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS
ASTM A959 (2004), A276, A312, A632, A176, A580
ASTM A959 (2004), A276, A312, A632, A176, A580
AVAILABILITY
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
CHEMICAL COMPOSITION (WEIGHT %) - UNS S30615
C (％): 0.16 ~ 0.24
Si (％): 3.20 ~ 4.00
Mn (％): ≤ 2.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.5
Ni (％): 13.5 ~ 16.0
Mo (％): -
Al (％): 0.80 ~ 1.50
Si (％): 3.20 ~ 4.00
Mn (％): ≤ 2.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.5
Ni (％): 13.5 ~ 16.0
Mo (％): -
Al (％): 0.80 ~ 1.50
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: Plate,sheet,strip
Tensile strength, σb/MPa: 620
Yield strength, σ0.2/MPa: 275
Elongation, δ(％): 35
Reduction of area, ф (％): -
Elongation, δ(％): 35
Reduction of area, ф (％): -
Hardness (HBW): 217
Hardness | HRB: 95
Cold bending property: N
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail sales@ccsteels.com
Hot search：S30615