Technical specifications JIS G4311 -1991 Martensitic Steel SUH616 Round bar, Flat bar, SUH616 Hot forging, Hot rolling, Heat treatment, 100% Ultrasonic test.
TECHNIAL DATA SHEET - Grade JIS SUH616
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resisting steel martensite Stainless steel
TECHNICAL STANDARDS - JIS G4311 -1991
CHEMICAL COMPOSITION (mass weight - %)
Annealed: 830 ~ 900, slow cooled
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.20 ~ 0.25
Silicon, Si (%): ≤ 0.50
Manganese, Mn (%): 0.50 ~ 1.00
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.020
Chromium, Cr (%): 10.0 ~ 13.0
Nickel, Ni (%): 0.50 ~ 1.00
Molybdenum, Mo (%): 0.75 ~ 1.25
Silicon, Si (%): ≤ 0.50
Manganese, Mn (%): 0.50 ~ 1.00
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.020
Chromium, Cr (%): 10.0 ~ 13.0
Nickel, Ni (%): 0.50 ~ 1.00
Molybdenum, Mo (%): 0.75 ~ 1.25
Tungsten, W (%): 0.75 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICEAnnealed: 830 ~ 900, slow cooled
Solution treated or Quenching: 1020 ~ 1070 oil cooled
Ageging treated or Tempering: ≥ 600 air cooled
Condition: Quenched and tempered
Tensile strength, σb/≥ MPa: 880
Yield strength, σ0.2/≥ MPa: 735
Elongation, δ ≥(%): 10
Reduction of area, ф ≥ (%): 25
Hardness | HBW ≤: 341.
Yield strength, σ0.2/≥ MPa: 735
Elongation, δ ≥(%): 10
Reduction of area, ф ≥ (%): 25
Hardness | HBW ≤: 341.
Suitable size (Diam. Thickness, Square size): 75mm max.
APPLICATION FIELD
Food processing equipments and parts.
Hydrometallurgy, heat exchangers, Oil and gas production equipments.
Food processing equipments and parts.
Hydrometallurgy, heat exchangers, Oil and gas production equipments.
Pulp mill bleach systems, Seawater handling equipments.
Tall oil distillation columns and equipments.
Tall oil distillation columns and equipments.
FORMS & DIMENSIONS
Round bar: Diam.5.5 ~ 450mm
Flat / Square bar: T15 ~ 350mm X W15 ~ 850mm
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 5000mm
Steel strip via cold rolled: T 1.0 ~ 3mm X W10 ~ 300mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Steel strip via cold rolled: T 1.0 ~ 3mm X W10 ~ 300mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search:SUH616
Previous page:4720H H47200
Last page:NCF600