Martensitic 12% Chromium bar and forge piece for Turbine blade Steel 10705BA Round bar, flat bar, plate, ESR 10705BA Turbine blade Tubings, Heat treatment.
TURBINE BLADE ALLOY - Grade 10705BA
Official Test Certification: issued by TUV - SGS - BV
Material Category: Martensitic 12% Chromium bars and forge piece for Turbine blades
Stock available - Round bar Diam. 55 ~ 200mm
Main Chemical composition (mass weight - %)
Carbon, C (％): 0.10 ~ 0.15
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): ≤ 0.60
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 11.50 ~ 13.5
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): ≤ 0.60
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): ≤ 0.60
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 11.50 ~ 13.5
Nickel, Ni (％): ≤ 0.60
Molybdenum, Mo (％): ≤ 0.60
Copper, Cu (%): ≤ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, Flat bar, Forge piece
Tensile strentgh, ab/MPa: 650
Yield strength σ0.2/MPa: 550
Yield strength σ0.2/MPa: 550
Elongation δ(％): 20.0
Reduction of area ф(％): 60.0
Hardness | HRB: 201 ~ 248
Reduction of area ф(％): 60.0
Hardness | HRB: 201 ~ 248
Impact Value (V-Notch charpy), RT: 35J
HEAT TREATMENT PRACTICE
Quenching: 980 ℃ min., oil cooled
Tempering: 710 ℃ min., air cooled
Stress relieving: 670 ℃, air cooled
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
The alloy is usually produced by BEF / AOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (Diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Disc (Diameter): 5.5mm to 850mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W50 ~ 1000mm X L1000 ~ 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：10705BA
Previous page：12CrWVNb
Last page：ASTM A182 Grade F93