SAE J405
2014-09-26 09:29:41 Origin： Remark：0 Click：
Ferrtic Stainless Steel S43600 ESR refined Round bar, J405 Hot forging / rolling, AISI 436 Heat treated, 100% Ultrasonic flaw detection test, Cold working, machined
MATERIAL DATA SHEET - SAE J405 & SAE 51436 & ASTM 436 & UNS S43600
MATERIAL CATEGORY: 17Cr-1Mo Ferritic steel
Equivalent materials to stainless steel grade 436
SAE 51436, SAE J405 (51436), UNS S43600, AISI 436
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.12
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 16.0 ~ 18.0
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.75 ~ 1.25
Niobium, Nb (％): 5 × C ~ 0.75
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 16.0 ~ 18.0
Nickel, Ni (％): -
Molybdenum, Mo (％): 0.75 ~ 1.25
Niobium, Nb (％): 5 × C ~ 0.75
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: heavy plate, sheet, strip
Tensile strength, σb/MPa: 450
Yield strength, σ0.2/MPa: 240
Elongation, δ (％): 22
Reduction of area, ф (％): -
Elongation, δ (％): 22
Reduction of area, ф (％): -
Hardness (HBW): 183
Hardness | HRB: 89
Cold bending property: 180D
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
Chemical equipments and parts.
Mechanical parts used in the condition of corrosion resistance.
Bolt and nuts, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 3mm to 500mm
Plate / Sheet steel / Steel strip: 1mm to 200mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Plate / Sheet steel / Steel strip: 1mm to 200mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE