STS630 H1075 Steel Ex-stock, STS630 H1075 Suppliers & Manufacturers, STS630 H1075 Forging Bar Plate machined, STS630 H1075 Exporters Technical specifications - KS D3706 - 2001 / 2006. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - KS D3706 Grade STS630
TECHNICAL SPECIFICATIONS: KS D3706 - 2001/2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 3.00 ~ 5.00
Mo (%): -
Cu (%): 3.00 ~ 5.00
Nb (%): 0.15 ~ 0.45
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1020 ~ 1060 Deg.C
Tensile strength, σb/ ≥ MPa:-
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 363
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1020 ~ 1060 Deg.C
Tensile strength, σb/ ≥ MPa:-
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 363
Aged H1075, 570 ~ 590 Deg.C, air cooled
Tensile strength, σb/ ≥ MPa:1000
Yield strength, σ0.2/ ≥ MPa: 865
Elongation, δ (％) ≥: 13.0
Reduction of area, ф (％) ≥: 45.0
Hardness ≤ (HBW): 302 min.
Tensile strength, σb/ ≥ MPa:1000
Yield strength, σ0.2/ ≥ MPa: 865
Elongation, δ (％) ≥: 13.0
Reduction of area, ф (％) ≥: 45.0
Hardness ≤ (HBW): 302 min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：H41350
Last page：STS630 H1150
Total list
Monthly rank
- 21ASTM A565 type 616HT
- 18X8CrMnN20-10
- 142Cr11NiMoNbVN
- 13AM-350
- 13X66Cr13
- 13ASTM A693 Gr. XM-16
- 13SUH310
- 13S42035
- 132Cr20Mn9Ni2Si2N
- 12STS321