STS630 H900
2020-02-12 12:38:45 Origin： Remark：0 Click：
STS630, a Martensitic stainless steel in Forms Round bar, flat bar, plate and forgings,STS630 Technical specifications - KS D3706 - 2001 / 2006. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment.
TECHNICAL DATA SHEET - Grade STS630 Aged H900
TECHNICAL SPECIFICATIONS: KS D3706 - 2001/2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel rod
CHEMICAL COMPOSITION (mass weight %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 3.00 ~ 5.00
Mo (%): -
Cu (%): 3.00 ~ 5.00
Nb (%): 0.15 ~ 0.45
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1020 ~ 1060 Deg.C
Aged H900, 470 ~ 490 Deg.C, air cooled
Tensile strength, σb/ ≥ MPa:1310
Yield strength, σ0.2/ ≥ MPa: 1175
Elongation, δ (％) ≥: 10.0
Reduction of area, ф (％) ≥: 40.0
Hardness ≤ (HBW): 375 min.
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1020 ~ 1060 Deg.C
Aged H900, 470 ~ 490 Deg.C, air cooled
Tensile strength, σb/ ≥ MPa:1310
Yield strength, σ0.2/ ≥ MPa: 1175
Elongation, δ (％) ≥: 10.0
Reduction of area, ф (％) ≥: 40.0
Hardness ≤ (HBW): 375 min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.