Specifications Custom 465 Datasheet, Ex-stock Custom 465 Suppliers, Inventory S46500 Property from steelmaking, Hot forging & Rolling, Heat treatment, Cold working.We also possess advanced precision machining equipments for further processing
MARTENSITIC STEEL DATASHEET - Custom 465
MATERIAL CATEGORY: Precipitation hardening type 12Cr-11Ni-1Mo-2Ti
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by BEF + AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
AVAILABILITY
Round bar / flat bar / strip / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / strip / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580, A564
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.020
Si (％): ≤ 0.25
Mn (％): ≤ 0.25
P (％)≤: 0.015
S (％)≤: 0.010
Cr (％): 11.0 ~ 12.5
Ni (％): 10.7 ~ 11.3
Mo (％): 0.75 ~ 1.25
N (&): -
Ti (％): 1.50 ~ 1.80
Si (％): ≤ 0.25
Mn (％): ≤ 0.25
P (％)≤: 0.015
S (％)≤: 0.010
Cr (％): 11.0 ~ 12.5
Ni (％): 10.7 ~ 11.3
Mo (％): 0.75 ~ 1.25
N (&): -
Ti (％): 1.50 ~ 1.80
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Forms: bar, steel plate, strip
Condition: solution treatment
Tensile strength, σb/MPa: 1215
Yield strength, σ0.2/MPa: 1100
Elongation, δ (％): 5.0
Reduction of area, ф (％): 34
Elongation, δ (％): 5.0
Reduction of area, ф (％): 34
Hardness | HRW: 361min, HRC 36min.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 610mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 610mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com