TECHNICAL DATA SHEET - ASTM A182 Grade FXM-11

MATERIAL TECHNICAL STANDARDS - ASTM A182 - 2018
MATERIAL TYPE - 20Cr-6Ni-9Mn Austenitic Stainless steel
HS CODE - 72221100 / 72221900
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     ≤ 0.040
Mn (%):   8.00 ~ 10.0
Si (%):    ≤ 1.00
P (%)≤:   0.060
S (%)≤:   0.030
Ni (%):    5.50 ~ 7.50
Cr (%):    19.0 ~ 21.5
Mo (%):   -
N (%):     0.15 ~ 0.40
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/MPa: 380
Elongation, δ ≥(%): 35.0
Reduction of area, ф ≥ (%): 55.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing (+AT)
Cooling medium: water or oil cooling
Tempering temperature: 1040 Deg.C
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 500mm
Square bar / Flat bar: 10mm to 1000mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry or help, pleased to E-mail 
our resident team of qualified production engineers, Email:
sales@ccsteels.com.

Hot search:FXM-11

Previous page:AMS 5581F
Last page:最后一页

Share to: