Description F65 Inventory, Specifications F65 Suppliers, Stocklist F65 Properties Bar Forging Ex-stock & Plate Heat treatment Machined, Rod Exporters Ex-stock Sale - Technical standards - ASTM A182 - 2018.or by agreement.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - ASTM A182 Grade F65
Material Technical Standards - ASTM A182 - 2018
Steel Material Type - 25Cr-7Ni-3Mo Ferritic - Austenitic Stainless steel
Customs HS Code - 72221100 / 72221900
Stocklist & Inventory - Diameter 25mm ~ 120mm
Chemical Composition ( Mass Weight % )
C (％): ≤ 0.030
Mn (％): 0.80 ~ 1.50
Si (％): ≤ 0.80
P (％)≤: 0.030
S (％)≤: 0.020
Ni (%): 5.80 ~ 7.50
Cr (%): 28.0 ~ 30.0
Mo (%): 1.50 ~ 2.60
N (%): 0.30 ~ 0.40
Cu (%): ≤ 0.80
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 750
Yield strength, σ0.2/MPa: 550
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing 1020 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 480mm
Square bar / Flat bar: 10mm to 620mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical inquiry or help, pleased to E-mail our resident team of qualified production engineers, Email: firstname.lastname@example.org.