ASTM A182 type S32808
2026-04-21 12:30:00 Origin： Remark：0 Click：
Description S32808 round bar, flat bar, plate, forgings properties heat treated, cold machined, Rod Exporters Technical standards - ASTM A182 - 2018
TECHNICAL DATASHEET - ASTM A182 type S32808
Technical standards: ASTM A182 - 2018
Customs HS Code - 72221100 / 72221900
Stockist & Inventory: diameter 80 mm
Chemical Composition (mass weight - %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 1.10
Phosphorus, P (％): ≤ 0.030
Sulfur, S (％): ≤ 0.010
Chromium, Cr (％): 27.0 ~ 27.9
Nickel, Ni (％): 7.00 ~ 8.20
Molybdenum, Mo (％): 0.80 ~ 1.20
Nitrogen, N (%): 0.30 ~ 0.40
Tungsten, W (％): 2.10 ~ 2.50
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 1.10
Phosphorus, P (％): ≤ 0.030
Sulfur, S (％): ≤ 0.010
Chromium, Cr (％): 27.0 ~ 27.9
Nickel, Ni (％): 7.00 ~ 8.20
Molybdenum, Mo (％): 0.80 ~ 1.20
Nitrogen, N (%): 0.30 ~ 0.40
Tungsten, W (％): 2.10 ~ 2.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb ≥ MPa: 700
Yield strength, σ0.2 / MPa: 500
Elongation, A5 ≥ (％): 15.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 321 max.
HEAT TREATMENT PRACTICE
Condition: solution annealing 1050 ~ 1150 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / rod (diameter): 6.0 ~ 500 mm
Square bar / flat bar: 10mm to 600 mm
Length: random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 300 X W20 ~ 1000 X L1000 ~ 3500 mm
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical inquiry or help, pleased to E-mail our resident team of qualified production engineers - Email: sales@ccsteels.com.
Hot search：S32808