X13CrMnNiN18-13-2 Stockist, X13CrMnNiN18-13-2 Equivalent Datasheet

X13CrMnNiN18-13-2
2022-09-24 08:32:22   Origin:   Remark:0 Click:

X13CrMnNiN18-13-2 is Non-magnetic austenitic stainless steel formulated for primary forming into wrought composition 18Cr-13Mn-2Ni-N type, it is availble in form of round bar, flat bar, hollow bars, produced from Hot working, cold machined.

 

MATERIAL TECHNICAL DATASHEET - Grade X13CrMnNiN18-13-2


OFFICIAL TEST CERTIFICATE: issued by TUV - SGS -  BV
MATERIAL CATEGORY: Austenitic type stainless 
steel
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): 11.0 ~ 14.0
Phosphorus, P (%)≤: 0.045
Sulfur, S (%)≤: 0.030
Chromium, Cr (%): 16.5 ~ 19.0
Nickel, Ni (%): 0.50 ~2.50
Nitrogen, N (%): 0.20 ~ 0.45
 
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: annealing 1050 ~ 1100 Deg. water cooled
Tensile strength, TS, σb/≥ MPa: 725
Yield strength, YS, σ0.2/≥ MPa: 355
Elongation, EL, δ ≥(%): 20.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 190 ~ 340
 
PRODUCT DESCRIPTION
The 
alloy
 is usually produced by IFF + AOD, EAF + VD, followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment or based on the buyer's special requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment or based on the buyer's special requirements.
 
PRODUCT PROFILE AND DIMENSIONS
Round bar (Diameter): 5.5 to 650mm
Square bar / Flat bar: T3 to 500 X W3 ~ 1200mm
Wire rod (Diameter):  1.0 to 16mm
Strip: T0.50~3.0 X W 8.0 ~ 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Other sizes can be supplied to meet specific requirements.
Other different shapes based on OEM.
 
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, please feel free to EMAIL our qualified production engineers E-mail: 
sales@ccsteels.com.

Hot search:X13CrMnNiN18-13-2

Previous page:X3NiCoMo18-8-5
Last page:1.2708

Share to: